ASAHI WA62J04I
ASAHI WA62J04I is solder wire for manual soldering, where you want to work with a wire that already has flux in the core. Here, the alloy is Sn62/Pb36/Ag2, and the flux is halogen-free with no-clean properties. In practice, this means it is made for general soldering tasks where you want a clean and controlled solder joint, usually without the need for subsequent cleaning.
The flux is classified as ROL0, and the residues are described as minimal and slightly yellowish. At the same time, the wire is specified with a flux content of 2.0 ± 0.2 wt%, giving a clear idea of how much active material is in the core. For manual soldering, a temperature above 320°C and a soldering time of 1–3 seconds are recommended.
For work in production and service, it is also practical that the wire is available in several diameters. This makes it possible to choose a thickness that suits the task, whether it is finer electronics work or more robust solder joints. The packaging sizes make it easy to choose a quantity that matches your consumption.
See datasheet from the manufacturer
See product video from the manufacturer
Typical applications
- Manual soldering in electronics production
- Service and repair tasks where no-clean soldering is desired
- Tasks where a halogen-free cored solder wire is desired
Specifications
- Manufacturer: ASAHI
- MPN: WA62J04I
- Alloy: Sn62/Pb36/Ag2
- Flux type: halogen-free, no-clean
- Flux classification: ROL0
- Flux content: 2.0 ± 0.2 wt%
- Recommended manual soldering temperature: >320°C
- Recommended soldering time: 1–3 seconds
- Available wire diameters: 0.5 mm, 0.6 mm, 0.8 mm, 1.0 mm, 1.2 mm, 1.6 mm, 2.0 mm
- Common packaging weights: 0.25 kg, 0.50 kg, 1.0 kg
The content is generated using AI - we reserve the right to make errors.
Contact HIN for further information about the product.