ASAHI WA62J08E solder wire
ASAHI WA62J08E is a cored solder wire for manual soldering, where the flux is already contained within the wire. This makes it practical when you want to work quickly and consistently without having to apply separate flux. The solder wire is based on the Sn62/Pb36/Ag2 alloy and uses FC5005 as a halogen-free no-clean core flux.
In practice, this means it is intended for tasks where a clean soldering process with minimal post-processing is desired. According to the data, the residues are small, slightly yellowish, and typically do not require cleaning. This is an advantage in general workshop work, where you want to keep the process simple while achieving a stable solder joint.
For manual soldering, a soldering temperature above 320°C and a soldering time of 1-3 seconds are recommended. This gives a clear picture of how the wire is used by hand: quickly, in a controlled manner, and with a focus on short heating times.
The wire is available in 0.8 mm diameter and 0.50 kg spools, among other options. The datasheet also indicates a shelf life of two years under proper storage conditions.
See datasheet from the manufacturer
See product video from the manufacturer
Typical applications
- Manual soldering in electronics work
- Repair and minor soldering tasks where a no-clean process is desired
- Work where minimal residue after soldering is desired
Specifications
- Manufacturer: ASAHI
- MPN: WA62J08E
- Alloy: Sn62/Pb36/Ag2
- Core flux: FC5005
- Flux type: Halogen-free, no-clean
- Flux content: 2.0 ± 0.2 wt%
- Flux classification: ROL0
- Recommended soldering temperature: >320°C
- Recommended soldering time: 1–3 seconds
- Available wire diameter: 0.8 mm
- Packaging: 0.50 kg (500 g) spool
- Residue: Minimal, clear yellowish tone, usually does not require cleaning
- Shelf life: 2 years under proper storage conditions
- EAN/GTIN: Not provided in the verified data