ASAHI WC63B16E
ASAHI WC63B16E is a flux-cored solder wire designed for general soldering applications where both tin/lead alloy and flux are required in the same wire. The alloy is Sn63Pb37, and the core contains CF-10 activated rosin flux. This makes the wire suitable for efficient soldering without the need to apply flux separately.
The flux is classified as ROH1 according to IPC J-STD-004, and the residues after soldering are described as light yellow and dry. This is a practical detail in production, as it results in a clear and relatively easy-to-manage residue after soldering.
The wire can be used for automatic, manual, rework, point, and brush soldering. The recommended soldering parameters are 270–350°C with a soldering time of 1–3 seconds. This makes it relevant in environments where controlled processes are used and stable soldering performance is desired.
Typical applications
ASAHI WC63B16E is typically used for soldering in electronics manufacturing, repairs, or tasks where there is a need to work quickly and precisely with a solder wire that already contains flux.
The wire is available in diameters from 0.5 to 2.0 mm, including 1.6 mm, and is supplied in standard packaging sizes of 0.25 kg, 0.50 kg, and 1.0 kg. This allows for the selection of a wire that suits both fine-detail work and more standard soldering tasks.
Specifications
- Manufacturer: ASAHI
- MPN: WC63B16E
- Alloy: Sn63Pb37
- Flux: CF-10 activated rosin flux
- Flux content: 2.0 ± 0.3 wt%
- Halide content: 0.7 wt%
- Flux classification: ROH1 (IPC J-STD-004)
- Residues: Light yellow and dry
- Recommended soldering temperature: 270–350°C
- Recommended soldering time: 1–3 seconds
- Application: Automatic, manual, rework, point, and brush soldering
- Available diameters: 0.5–2.0 mm
- Packaging sizes: 0.25 kg, 0.50 kg (500 g), 1.0 kg
The content is generated using AI - we reserve the right for errors.